Effect of basic fibroblast growth factor on cartilage regeneration

Document Sample
Effect of basic fibroblast growth factor on cartilage regeneration Powered By Docstoc
					Effect of basic fibroblast growth factor on cartilage regeneration
          in chondrocyte-seeded collagen sponge scaffold


     Toshia FUJISATO, Toshinobu SAJIKI, Qiang LIU, and Yoshito IKADA



            Research Center for Biomedical Engineering, Kyoto University

              53 Kawahara-cho, Shogoin, Sakyo, Kyoto 606-01, JAPAN




ABSTRACT



A chondrocyte-collagen composite was prepared in an attempt to regenerate

cartilage by its subcutaneous implantation in nude mouse.                  When the

composite was impregnated with basic fibroblast growth factor (bFGF) prior to

implantation, regeneration of the cartilage tissue was remarkably accelerated.

Histological staining of the implanted composites with safranin O -fast green

revealed that the cells incorporated in the composites exhibited their

phenotype and formed a new matured cartilage.             A thin layer of fibrous

capsule was observed surrounding the implanted composite and the

inflammatory response of the host to the implant was mild.                   Specific

proteoglycans were accumulated in the composite even 1 week after

implantation. At 2 weeks after implantation, the chondrocytes regenerated the

cartilage tissue, although still immatured, but at 4 weeks almost all of the

chondrocytes transferred to the matured stage. On the contrary, such matured

cartilage tissue was not noticed up to 4 weeks after implantation, if the collagen

scaffold was not impregnated with bFGF. Moreover, the matured area was
T.Fujisato et al.                        Effect of bFGF on cartilage regeneration



limited to only a small fraction of the implanted composite, unless bFGF was

incorporated in it.



Keywords: bFGF, chondrocyte, cartilage regeneration, collagen, angiogenesis, tissue

engineering



Correspondence to Professor Y.Ikada.

Fax: +81-75-751-4144




                                       -2-
T.Fujisato et al.                         Effect of bFGF on cartilage regeneration



INTRODUCTION



Recently much attention has been paid on the use of biodegradable polymers

to regenerate metabolic organs such as the liver1,2 and intestine 3 and to

reconstruct structural tissues like cartilage 4-9, bone8-10, and urothelial

structure 11 by cell transplantation12-14. In clinics, cartilage replacement is also

needed, especially in maxillofacial, orthopedic, and plastic surgery. Mostly,

silicone prosthesis and autologous rib bones have been used for this purpose,

but several problems are involved in these cartilage replacements, such as

infection at the interface between the implanted material and the tissue, and

deterioration of the donor site by the filling with fibrous cartilage tissue.

Therefore, a preferable replacement would be to use the natural cartilage

tissue.     The first attempt to use the cultured chondrocytes for an articular

cartilage repair was reported by Green et al.15 and it is supposed that a

template is necessary for cartilage reconstruction by chondrocytes in vivo.

There are some reports describing the seeding of collagen and other porous

matrices with chondrocytes for this purpose 4-9. Itay et al. reported the repair of

bone tissue by chondrocytes incorporated in collagen gel as a template.

Langer, Vacanti, and their coworkers have developed a tissue engineering

technique with the use of chondrocytes of the target region. The cells will be

isolated from patients, proliferated by the in vitro culture to a higher density,

and then implanted after preparing a chondrocyte-polymer composite as the

core for the cartilage reconstruction. It is reported that chondrocytes can be

isolated from tissue and grown in culture in such a way as to maintain their

phenotype 15-18.

          In this work, a chondrocyte-collagen composite is prepared in an attempt

to regenerate the cartilage by its implantation in mouse. To diminish the



                                        -3-
T.Fujisato et al.                       Effect of bFGF on cartilage regeneration



difficulty associated with autograft transplantation, nude mice were used for

the implantation of the composite. As a scaffold for the cartilage regeneration,

a porous collagen sponge is employed.         Collagen has been used as the

scaffolds for tissue regeneration19,20. We have also reported that it is an

excellent template to regenerate skin21 and esophageal replacement22. When a

bilayer artificial skin composed of an outer layer of silicone and an inner

sponge layer of collagen was placed on the skin defect on the backs of rats, it

was observed that epidermal cells migrated from the edge of the wound

between the two layers 21. An artificial esophagus with a bilayered structure

made of porous collagen sponge and silicone was studied to promote tissue

regeneration by collagen, and the collagen sponge was replaced by autologous

tissue and regeneration of the “neoesophagus” was observed 2 weeks after

implantation22.     In our previous work, chondrocyte-poly(lactic acid) (PLA)

complex was prepared to study its potentiality for cartilage reconstruction, but

no matured cartilage tissue was observed in 1 month after implantation 23. This

suggests that supplying nutrients to the seeded cells in the early stage of

transplantation to maintain them alive and promote tissue regeneration is very

important. An effective means for this purpose may be to induce the capillary

formation around the implanted composite by giving an angiogenic factor like

basic fibroblast growth factor (bFGF)24. In addition to the angiogenesis, bFGF

is known to perform other important functions such as parenchymal cell

proliferation, differentiation25,26, and promotion of cartilage repair in vivo

although cartilage is an avascular tissue 27,28. In this study, bFGF was applied

to the chondrocyte-collagen composite prior to implantaion.




MATERIALS AND METHODS



                                      -4-
T.Fujisato et al.                       Effect of bFGF on cartilage regeneration




Collagen sponge

       A collagen sponge as the scaffold was prepared from 0.3% hydrochloric

solution of type I atelocollagen (Cell matrix ®; Nitta Gelatin Co. Ltd., Osaka,

Japan, pH=3.0). The collagen solution was stirred at 2000 rpm for 1 hr at 4 °C to

generate small bubbles and then freeze-dried.       The resulting sponge was

vacuum-dried for 24 hrs at 105 °C, immersed in 0.2% acetic acid solution of

glutaraldehyde for 24 hrs at 4 °C to introduce chemical crosslinking, and

pressed to a sheet of 3 mm thickness. The average pore size, pore volume

fraction, and density of the sponge were 86 µm, 87%, and 1.010-2 g/cm3,

respectively.       The sponge sheet was cut to have a round shape of 9 mm

diameter. Two pieces of round sheets were overlapped each other and then

sewn together with 7-0 polypropylene suture.          The lapped sponge was

immersed overnight in 70% ethanol for sterilization and then washed with

phosphate buffered saline (PBS; Nissui pharmaceutical Co. Ltd., Tokyo, Japan,

pH=7.4). Prior to implantation, the collagen sponge was impregnated with

bFGF by immersing in the 80 µg/ml PBS solution of bFGF for 24 hrs at 4 °C,

unless otherwise stated. bFGF was kindly supplied by Kaken Pharmaceutical

Co. Ltd., Tokyo, Japan. The amount of bFGF was determined by HPLC using a

heparin column.



Chondrocytes

       Chondrocytes were isolated from the costal cartilage of rats by

collagenase digestion29. Costae were removed from sacrificed rats and the

cartilage was isolated carefully from them, so that fibrous tissues were not

included. The isolated cartilage was minced by surgical scissors and immersed

in 0.25% trypsin-0.05% collagenase (Amano Pharmaceutical Co. Ltd., Osaka,



                                       -5-
T.Fujisato et al.                        Effect of bFGF on cartilage regeneration



Japan) solution for 1 hr. After 3 times washing with PBS, the treated pieces of

cartilage were immersed in 0.02% ethylenediaminetetraacetic acid (EDTA)

solution for 1 hr. After washing, they were put on a petri dish for tissue culture

(Corning® Type 25020; Corning Co. Ltd., NY), incubated for about 3 weeks

adjusting the level of medium so as not to float the minced tissues in the

medium, and then the migrated cells were collected by a cell harvesting

solution (0.25% trypsin-0.02% EDTA in PBS).              Eagle's MEM (Nissui

Pharmaceutical Co. Ltd.) was used as culture medium with 10% fatal bovine

serum (Bio Whittaker, Inc., Maryland).        One hundred µl of chondrocyte

suspension containing 1106 cells was carefully injected with a 27 G needle

syringe into the center of lapped collagen sponge disk. The cell -injected

sponge was stored in CO 2 incubator for 2 hrs to allow the cells to adhere to the

collagen sponge before implantation as much as possible.



Cell culture

       For the in vitro study, the chondrocyte suspension or the chondrocyte-

collagen composite was put into a 24 well-micro plate for tissue culture

(Corning® Type 258201; Corning Co. Ltd.).          The cell density was 1,000

cells/well in the case of chondrocyte suspension.         Culture medium was

exchanged everyday.      After predetermined periods of time, the cells were

counted by measuring the activity of lactate dehydrogenase (LDH) in the cells

using a test kit for clinical use (LDH monotest ®; Boehringer Manheim,

Germany) after complete        cell   digestion by 0.1% polyoxyethylene(10)

octylphenyl ether (Triton® X-100; Wako Pure Chemical Industries, Ltd., Osaka,

Japan)30.



Implantation



                                       -6-
T.Fujisato et al.                        Effect of bFGF on cartilage regeneration



       Animals were carefully reared in the Research Center for Biomedical

Engineering, Kyoto University, according to the guideline of Kyoto University

for Animal Experiments. All animals were anesthetized with diethyl ether and

pentobarbital sodium for the release of suffering from the pain during

operation. Two samples of chondrocyte-collagen composite and the control

without chondrocytes were subcutaneously implanted into the back of a male

nude mouse. The mice were divided into 2 groups receiving collagen sponges

with bFGF and without bFGF. Twelve mice were employed in each group.

After predetermined periods of time, the sponges were explanted and

subjected to gross and microscopic observation and a histological study to

evaluate the inflammatory response of the host and cartilage matrix secretion.

Explanted samples were fixed with 10% formaldehyde aqueous solution,

replaced with ethanol, and embedded in paraffin. The fixed samples were

sectioned to 10 µm thickness with a microtome at 3 different distances from the

surface of samples, and stained with Mayer’s Haematoxylin-Eosin (H.E.)

solution. In addition to the conventional H.E. staining, safranin O -fast green

staining was applied for identifying the cartilage proteoglycans 31.




RESULTS



bFGF impregnation

       The processes of chondrocyte-collagen composite preparation are

schematically represented in Figure 1. The collagen sponge disk was placed in

plenty of 80 µg/ml bFGF solution in PBS to incorporate bFGF into the disk.

Figure 2 shows the plot of bFGF amount adsorbed into the disk at 37 °C as a

function of time.    As is seen, the bFGF impregnation seems to come to



                                      -7-
T.Fujisato et al.                        Effect of bFGF on cartilage regeneration



saturation after 30 hr incubation, reaching a leveling-off value of 60 µg per mg

of collagen sponge. An addition of serum albumin (BSA) to the bFGF solution

had no significant effect on the bFGF impregnation.          The release of the

adsorbed bFGF into PBS upon immersion of the impregnated sponge in PBS at

37 °C is shown in Figure 3. The bFGF impregnation was carried out at 4 and 37

°C. Clearly, approximately 90% of the bFGF impregnated even at 4 °C for

minimizing the bFGF deactivation still remains in the interior of the collagen

sponge. The bFGF remaining in the sponge is expected to be released upon

enzymatic degradation of the crosslinked collagen when the sponge disk is

implanted in mice.



Chondrocyte seeding

       Rat chondrocytes were seeded in the collagen sponge disk after

trypsinization of the cultured cells isolated from the rat costal cartilage on a

petri dish for tissue culture with cell harvesting solution. Figure 4 shows the in

vitro growth of the chondrocytes after trypsinization on the 24 well-micro plate.

Obviously, cell confluency is obtained upon incubation for about 5 days. As a

preliminary study to determine the effective method for seeding the

chondrocytes in the matrix, cells were seeded in the collagen sponge with three

different methods; 1. injection of the cell suspension in culture medium to the

sponge with a needle at 25 °C, 2. injection of the cell suspension in culture

medium containing 0.3% collagen to the sponge with a needle at 4 °C, and 3.

immersion of the sponge disk into the cell suspension in culture medium at 25

°C in 24 well-micro plate. Two hrs after cell seeding, the disks were washed

with PBS to remove the non-seeded chondrocytes, and the number of cells was

estimated from the activity measurement of LDH.            Figure 5 shows the

percentage of the chondrocytes still remaining in the interior of the sponge



                                       -8-
T.Fujisato et al.                        Effect of bFGF on cartilage regeneration



disks after washing. As can be seen, about 50% of the cells remain adhered to

the collagen sponge when a needle is used, regardless of the presence of

collagen in the cell suspension. In the following study we employed the 1st

method for the cell seeding, that is, injection of the cell suspension containing

1106 cells and bFGF through a needle.

        The chondrocytes seeded in the collagen sponge were further incubated

for their stronger adhesion to the collagen surface. Figure 6 shows the result of

cell growth in the collagen sponge determined by LDH activity. It is seen that

the cell density slowly increases with the incubation time. The decreased cell

density on day 9 is probably due to the cell injury caused after reaching

confluency. The addition of bFGF to the culture medium had no effect on the in

vitro cell growth.   Figure 7 demonstrates a SEM microphotograph of the

chondrocytes attached to the collagen surface after 3 days of incubation. As is

apparent, the cell is spreading on the collagen substrate.



Composite implantation

        The chondrocyte-seeded collagen composite with or without bFGF was

subcutaneously implanted in nude mice to study the effect of bFGF addition.

In our previous work, the collagen sponge carrying neither chondrocytes nor

bFGF disappeared as a result of collagen biodegradation when i mplanted for

longer than 25 weeks. On the other hand, remarkable angiogenesis was noticed

around the collagen disk when bFGF had been incorporated in the sponge,

independent of the presence of chondrocyte.            A representative optical

photograph of nude mouse with implanted collagen sponges is shown in

Figure 8. The sponges were implanted for 4 weeks after impregnation with

bFGF.     As can be seen, the presence of implanted sponge is no more

recognizable unless the sponge is seeded with chondrocytes, whereas we can



                                       -9-
T.Fujisato et al.                         Effect of bFGF on cartilage regeneration



clearly notice the sponge from the outside of the mouse if chondrocytes are

seeded in the collagen sponge.

       Optical photographs of sponges implanted for 1 week with and without

bFGF are shown in Figure 9. Obviously, we cannot see any angiogenesis if the

collagen sponge contained neither bFGF nor chondrocytes, whereas seeding of

chondrocytes in the sponge induced angiogenesis even if chondrocyte was not

seeded.      Impregnation of the sponge with bFGF markedly enhanced

angiogenesis, regardless of chondrocyte seeding.         When the chondrocyte-

collagen composite was implanted for 4 weeks together with bFGF, the

formation of cartilage was clearly noticed.      An optical photograph of the

cartilage formed by 4 week implantation of the chondrocyte-collagen

composite is shown in Figure 10. The soft sponge became smaller in size and

less flexible. The size decrease became more prominent with the increasing

density of seeded cells. The size dependence on the density of seeded cells

after 2 weeks of implantation is shown in Figure 11.

       To assess the cartilage regeneration, we stained the cross-section of the

explanted collagen composites with safranin-O fast green. The result for the

chondrocyte-collagen composites implanted for 4 weeks in mice is given in

Figure 12. The area with the regenerated cartilage should be stained strongly

reddish with this dye as a result of metachromasia 31.         Figure 12 clearly

indicates that only a very small fraction of the composite cross-section shows

metachromasia unless bFGF is incorporated in the collagen sponge, whereas

most of the cross-section of the composite impregnated with bFGF and seeded

with chondrocytes exhibit strong metachromasia supporting the cartilage

formation. The staining of explants with safranin O-fast green revealed that

chondrocytes could produce specific proteoglycans only after 1 week of

implantation.       However, even at 2 weeks after implantation, chondrocytes



                                       - 10 -
T.Fujisato et al.                        Effect of bFGF on cartilage regeneration



could regenerate the cartilage tissue, although immatured, and at 4 weeks after

implantation, almost all of the chondrocytes transferred to the matured stage.

Without impregnating the collagen sponge with bFGF, such a matured

cartilage tissue was not observed up to 4 weeks after implantation.

       H.E. staining of the implanted composites showed that a thin layer of

fibrous capsule was formed surrounding the implanted composites with a mild

inflammatory response of the host to the implants (Figure 12).




DISCUSSION



To regenerate tissues and maintain their biological functions, individual cells

will be probably collected from the organ or tissue of patients, followed by

attachment of the cells to a bioabsorbable polymer scaffold by a culture

technique. The resulting cell-polymer composite is generally implanted at a

site where the cells can grow and effectively express their function.

Chondrocytes are parenchymal cells like hepatocytes, but it is reported that

they exhibit much more remarkable proliferation and cartilage formation even

in vitro if the culture condition is adequate 15-18.         This suggests that

reconstruction of the cartilage tissue is easier than that of the liver. In a

previous work, a hepatocyte- or chondrocyte-PLA complex was prepared to

study its potentiality for liver regeneration and cartilage reconstruction 23. The

measurement of the protein production from the cells as an index of cell

function and expression of their phenotypes revealed that hepatocytes did not

undergo any growth and gradually diminished their function of albumin

biosynthesis on the PLA substrate in vitro. On the contrary, chondrocytes grew

well even on culture dishes and produced type II collagen, which became



                                      - 11 -
T.Fujisato et al.                        Effect of bFGF on cartilage regeneration



maximal on the 10th day after cultivation. This is simply because the cell

density increased to the highest level by 10 day cultivation, reaching the

confluent state and decreased gradually after the 10th day. This indicates that

chondrocytes produced smaller amounts of collagen under the confluent

condition than prolifelative stage. In the case of hepatocytes, a multicellular

colony was seen in the scaffold, in contrast to the seeded chondrocytes which

spread dispersively throughout the scaffold.

       When the chondrocyte-collagen composite was implanted into nude

mice, injection of any immunosuppressive agent was not necessary even in the

xenograft implantation.     From the histological staining of the implanted

composites with safranin O-fast green which can bind to negatively charged

glycosaminoglycans in cartilage, it is obvious that the implanted cells exhibited

their phenotype in vivo and formed a new matured cartilage in addition to the

morphological characteristics (Figure 12). On the contrary, implantation of

collagen scaffolds without cultured chondrocytes did not result in formation of

new cartilage at all.

       Quick formation of capillaries around the implanted composite seems

necessary to maintain the seeded cells alive and promote tissue reconstruction.

Therefore, bFGF, a well-known angiogenic factor, was incorporated into the

collagen sponge, although cartilage is an avascular tissue. Expectedly, a lot of

small blood vessels were observed around the matrix when the collagen

scaffold was impregnated with bFGF (Figure 9). This strongly suggests that the

use of angiogenic factor is very effective for blood vessel formation around the

complex, which may promote the cartilage formation. Indeed, acceleration of

cartilage reconstruction by bFGF incorporated in the composite was noticed as

demonstrated above. It has been proposed that cartilage tissue is transformed

to bone tissue if vascular invasion occurs and chondrocytes terminally



                                      - 12 -
T.Fujisato et al.                         Effect of bFGF on cartilage regeneration



differentiate to hypertrophic chondrocytes which produce high levels of

alkaline phosphatase. During this study we did not observe any differentiation

of chondrocytes. It is interesting to point out that bFGF is reported to promote

cartilage repair in vivo27 and inhibit the terminal differentiation of chondrocytes

and calcification28. The formation of small blood vessels around the collagen

sponge became the most remarkable at 1 week after implantation with bFGF

and then diminished gradually.           The histological study suggests that

chondrocytes would be in the proliferative stage in the first 2 weeks and then

transferred in the matured stage. More detailed histological and long-term

implantation are needed to follow the fate of the regenerated cartilage.

       Any significant effect of bFGF addition on the in vitro proliferation of

chondrocytes was not observed, compared with the in vivo result (Figure 9).

This is probably because bFGF did not influence the chondrocyte growth

directly, but caused angiogenesis around the implanted tissue, which in turn

affected the cartilage regeneration. Freed et al. observed neochondrogenesis

without using any angiogenic factor when chondrocytes were seeded on

fibrous polyglycolic acid and porous PLA 7.           We implanted hepatocyte-

collagen composites with bFGF in nude mice, but cell viability was not

improved by the bFGF addition32. This indicates that bFGF is not always

effective to accelerate the tissue regeneration. Other kinds of growth factor

such as transforming growth factor also might affect cell proliferation and

differentiation.    In the present work, the in vivo release of bFGF from the

collagen sponge containing bFGF could not be determined, as the in vivo

release rate was too difficult to measure. It is very likely that the in vivo release

of bFGF accompanies the collagen biodegradation in the body.




                                       - 13 -
T.Fujisato et al.                      Effect of bFGF on cartilage regeneration



CONCLUSIONS



It may be concluded that chondrocytes seeded onto a collagen scaffold can

proliferate, express their distinct phenotype, and mature quickly, especially

when the scaffold is impregnated with bFGF.       Thus, the composite from

chondrocytes and the collagen sponge carrying bFGF is very promising for the

tissue engineering of cartilage reconstruction. More detailed histological and

long-term implantation studies are currently under way.




                                    - 14 -
T.Fujisato et al.                         Effect of bFGF on cartilage regeneration



REFERENCES



1    Fontaine M, Hansen LK, Thompson S et al. Transplantation of genetically

     altered hepatocytes using cell-polymer constructs. Transplant Proc 1993;

     25: 1002-1004.

2    Wald HL, Sarakinos G, Lyman MD, Mikos AG, Vacanti JP, Langer R. Cell

     seeding in porous transplantation devices. Biomaterials 1993; 14: 270-278.

3    Mooney DJ, Organ G, Vacanti JP, Langer R. Design and fabrication of

     biodegradable polymer devices to engineer tubular tissues. Cell Transplant

     1994; 3: 203-210.

4    Itay S, Abramovici A, Nevo Z.              Use of cultured embryonal chick

     epiphyseal chondrocytes as grafts for defects in chick articular cartilage.

     Clin Orthop 1987; 220: 284-303.

5    Puelacher WC, Kim SW, Vacanti JP, Schloo B, Mooney D, Vacanti CA.

     Tissue-engineered growth of cartilage: the effect of varying the

     concentration of chondrocytes seeded onto synthetic polymer matrices. Int

     J Oral Maxillofac Surg 1994; 23: 49-53.

6    Vacanti CA, Paige KT, Kim WS, Sakata J, Upton J, Vacanti JP.

     Experimental tracheal replacement using tissue-engineered cartilage. J

     Pediatr Surg 1994; 29: 201-205.

7    Freed LE, Marquis JC, Nohria A, Emmanual J, Mikos AG, Langer R.

     Neocartilage formation in vitro and in vivo using cells cultured on

     synthetic biodegradable polymers. J Biomed Mater Res 1993; 27: 11-23.

8    Vacanti CA, Vacanti JP. Bone and cartilage reconstruction with tissue

     engineering approaches. Otolaryngol Clin North Am 1994; 27: 263-276.

9    Vacanti CA, Kim W, Upton J et al. Tissue-engineered growth of bone and

     cartilage. Transplant Proc 1993; 25: 1019-1021.



                                       - 15 -
T.Fujisato et al.                         Effect of bFGF on cartilage regeneration



10   Thomson RC, Yaszemski MJ, Powers JM, Mikos AG. Fabrication of

     biodegradable polymer scaffolds to engineer trabecular bone. J Biomater

     Sci Polymer Edn 1995; 7: 23-38.

11   Atala A, Freeman MR, Vacanti JP, Shepard J, Retik AB. Implantation in

     vivo and retrieval of artificial structures consisting of rabbit and human

     urothelium and human bladder muscle. J Urol 1993; 150: 608-612.

12   Langer R, Vacanti JP. Tissue engineering. Science 1993; 260: 920-926.

13   Mikos AG, Sarakinos G, Leite SM, Vacanti JP, Langer R. Laminated three-

     dimensional biodegradable foams for use in tissue engineering.

     Biomaterials 1993; 14: 323-330.

14   Mikos AG, Lyman MD, Freed LE, Langer R. Wetting of poly(L-lactic acid)

     and poly(DL-lactic-co-glycolic acid) foams for tissue culture. Biomaterials

     1994; 15: 55-58.

15   Green WT Jr. Articular cartilage repair. Behavior of rabbit chondrocytes

     during tissue culture and subsequent allografting. Clin Orthop 1977; 124:

     237-250.

16   Binderman I, Greene RM, Pennypacker JP. Calcification of differentiating

     skeletal mesenchyme in vitro. Science 1979; 206(4415): 222-225.

17   Suzuki F.       Osteogenesis by chondrocytes from growth cartilage.

     Tanpakushitu Kakusan Koso 1978; 23: 1303-1311.

18   Suzuki F. Hormonal effects on expression of the differentiated phenotype

     of chondrocytes in culture. Taisha 1982; 19: 729-736.

19   Yannas IV, Lee E, Orgill DP, Skrabut EM, Murphy GF. Synthesis and

     characterization of a model extracellular matrix that induces partial

     regeneration of adult mammalian skin. Proc Natl Acad Sci USA 1989; 86:

     933-937.




                                       - 16 -
T.Fujisato et al.                          Effect of bFGF on cartilage regeneration



20   Matsuda T, Akutsu T, Kira K, Matsumoto H. Development of hybrid

     compliant graft: rapid preparative method for reconstruction of a vascular

     wall. ASAIO Trans 1989; 35: 553-555.

21   Matsuda K, Suzuki S, Isshiki N, Ikada Y. Re-freeze dried bilayer artificial

     skin. Biomaterials 1993; 14: 1030-1035.

22   Natsume T, Ike O, Okada T, Takimoto N, Shimizu Y, Ikada Y. Porous

     collagen sponge for esophageal replacement. J Biomed Mater Res 1993; 27:

     867-875.

23   Ito K, Fujisato T, Ikada Y. Implantation of cell-seeded biodegradable

     polymers for tissue reconstruction. Mat Res Soc Symp Proc 1992; 252: 359-

     365.

24   Broadley KN, Aquino AM, Woodward SC et al. Monospecific antibodies

     implicate basic fibroblast growth factor in normal wound repair. Lab Invest

     1989; 61: 571-575.

25   Slack JMW, Darlington BG, Health JK, Godsave SF. Mesoderm induction

     in early Xenopus embryos by heparin-binding growth factors. Nature 1987;

     326: 197-200.

26   Kimelman D, Abraham JA, Haaparanta T, Palisi TM, Kirschner MW. The

     presence of fibroblast growth factor in the frog egg: its role as a natural

     mesoderm inducer. Science 1988; 242: 1053-1056.

27    Cuevas P, Burgos J, Baird A. Basic fibroblast growth factor (FGF)

      promotes cartilage repair in vivo. Biochem Biophys Res Commun 1988; 156:

      611-618.

28    Kato Y, Iwamoto M.          Fibroblast growth factor is an inhibitor of

      chondrocyte terminal differentiation. J Biol Chem 1990; 265: 5903-5309.

29   Shimomura Y, Yoneda T, Suzuki F. Osteogenesis by chondrocytes from

     growth cartilage of rat rib. Calcif Tiss Res 1975; 19: 179-187.



                                        - 17 -
T.Fujisato et al.                            Effect of bFGF on cartilage regeneration



30   Tamada Y, Kulik EA, Ikada Y. A simple method for platelet counting.

     Biomaterials; in press.

31   Pedrini        MA,   Maynard   JA,   Pedrini   VA.      Pseudoachondroplasia:

     biochemical and histochemical studies of cartilage. J Bone Joint Surg Am

     1984; 66: 1408-1414.

32   Morikawa N, Fujisato T, Tabata Y, Ikada Y. Implantation of hepatocyte-

     seeded polymer scaffold. Paper presented at the 23rd Symposium of Medical

     Polymers, 16-17 June 1994, Tokyo, Japan.




                                          - 18 -
T.Fujisato et al.                           Effect of bFGF on cartilage regeneration



Captions to Figures



Figure 1. Preparation scheme of rat chondrocyte-collagen sponge composite

            and its subcutaneous implantation into mouse.



Figure 2. Time course of the collagen sponge impregnation with bFGF from its

            solution at 37 °C. (The initial concentration of bFGF in PBS = 80

            µg/ml)



Figure 3. In vitro release of bFGF from the impregnated collagen sponge at 37

            °C into PBS.

            (E) Incubation at 37 °C for 10 hrs prior to the release test.

            (J) Incubation at 4 °C for 8 hrs and then 37 °C for 2 hrs prior to the

            release test.



Figure 4. Growth of rat chondrocytes cultured on 24 well-micro plate for

            tissue culture.



Figure 5. Chondrocytes adhered to the collagen sponge after washing with

            culture medium when they were applied with three different

            methods. (The initial cell density = 5106 cells/sponge)

            (1) Injection of cell suspension in culture medium with a needle at 25

            °C.

            (2) Injection of cell suspension in culture medium containing 0.3%

            collagen with a needle at 4 °C.

            (3) Immersion of the sponge disk into the cell suspension in culture

            medium at 25 °C in 24 well-micro plate.



                                         - 19 -
T.Fujisato et al.                         Effect of bFGF on cartilage regeneration




Figure 6. In vitro growth of rat chondrocytes in the collagen sponge.



Figure 7. SEM of rat chondrocytes attached to the collagen sponge.                 A

            indicates chondrocyte and B collagen sponge.



Figure 8. Photograph of nude mouse 4 weeks after subcutaneous implantation

            of      the   bFGF-impregnated      composites   with       and   without

            chondrocytes.



Figure 9. Various collagen sponges after 1 week subcutaneous implantation.



Figure 10. Transformation of the chondrocyte-collagen composite to a cartilage

            lump 4 weeks after subcutaneous implantation.



Figure 11. Effect of the chondrocyte density on the volume change of the

            chondrocyte-collagen    composite      with   bFGF      2   weeks   after

            implantation.



Figure 12. Cross-sections of chondrocyte-collagen composite with and without

            bFGF 4 weeks after implantation.

            (a) without bFGF and (b) with bFGF.




                                       - 20 -

				