					Table A.1        Variation in Low-Amplitude Shear Wave Velocity, Low-Amplitude Shear Modulus, Low-Amplitude Material
                 Damping Ratio and Estimated Void Ratio with Isotropic Confining Pressure from RC Tests of Reconstituted SM Specimen

                                                                                Low-Amplitude Low-Amplitude
                                                     Low-Amplitude Shear
     Isotropic Confining Pressure, so '                                          Shear Wave Material Damping  Estimated
                                                        Modulus, Gmax
                                                                                 Velocity, Vs   Ratio, Dmin  Void Ratio, e
   (psi)             (psf)            (kPa)          (ksf)          (MPa)             (fps)                 (%)
    1.5              216               10             716            34.3             472                   1.48         0.683
    2.0              288               14             796            38.1             498                   1.34         0.683
     4               576               28            1045            50.1             570                   1.07         0.683
     8               1152              55            1441            69.1             670                   0.86         0.681
    16               2304              110           1934            92.7             775                   0.79         0.678
     4               576               28             903            43.3             523                   1.76         0.629

Table A.2        Variation in Shear Modulus, Normalized Shear Modulus and Material Damping Ratio with Shearing Strain
                 from RC Tests of Reconstituted SM Specimen; Isotropic Confining Pressure (Loading), so' = 4 psi (0.58 ksf = 28 kPa)
                                              Normalized                      Material                          Material
                                                            Average+                       Shear Modulus, G,
                 Peak Shearing Shear Modulus,   Shear                                   x                    Damping Ratio,
                                                                           Damping Ratio ,    after Peak
                   Strain, %       G, ksf     Modulus, G/ Shearing Strain,                                    D, after Peak
                                                                %              D, %          Sheaering, ksf
                                                 Gmax                                                         Sheaering, %
                   5.38E-04        1074          1.00       5.38E-04           1.12               -*                -*
                   9.80E-04        1049          0.98       9.80E-04           1.29              1074             1.20
                   1.80E-03        1009          0.94       1.80E-03           1.63              1066             1.35
                   3.17E-03         962          0.90       2.83E-03           1.85              1065             1.19
                   5.52E-03         886          0.83       4.81E-03           2.28              1050             1.24
                   9.97E-03         792          0.74       8.30E-03           3.11              1025             1.46
                   1.62E-02         693          0.65       1.27E-02           4.33              989              1.61
             + Average Shearing Strain from the First Three Cycles of the Free Vibration Decay Curve
             x Average Damping Ratio from the First Three Cycles of the Free Vibration Decay Curve
             * Not Measured because Shearing Strain is Low

Table A.3        Variation in Shear Modulus, Normalized Shear Modulus and Material Damping Ratio with Shearing Strain
                 from TS Tests of Reconstituted SM Specimen; Isotropic Confining Pressure (Loading), so' = 4 psi (0.58 ksf = 28 kPa)
                             First Cycle                                                      Tenth Cycle
   Peak            Shear       Normalized     Material                                                     Material
                                                           Peak Shearing Shear Modulus, Normalized Shear
 Shearing        Modulus, G, Shear Modulus, Damping Ratio,                                               Damping Ratio,
                                                             Strain, %       G, ksf     Modulus, G/Gmax
 Strain, %          ksf          G/Gmax        D, %                                                         D, %
 3.54E-04            1123             1.00           0.77          3.51E-04           1128                  1.01          0.82
 7.08E-04            1112             1.00           0.89          7.09E-04           1106                  0.99          0.94
 1.08E-03            1094             0.98           1.09          1.08E-03           1093                  0.98          1.09
 2.27E-03            1033             0.92           1.81          2.28E-03           1028                  0.92          1.69
 6.52E-03            901              0.81           3.54          6.60E-03            891                  0.80          3.19
 9.76E-03            804              0.72           4.73          9.81E-03            802                  0.72          4.36




                                                                 V. 22
Table A.4        Variation in Shear Modulus, Normalized Shear Modulus and Material Damping Ratio with Shearing Strain
                 from RC Tests of Reconstituted SM Specimen; Isotropic Confining Pressure (Loading), so' = 16 psi (2.3 ksf = 110 kPa)
                                              Normalized                     Material                          Material
                                                                 Average+                 Shear Modulus, G,
                 Peak Shearing Shear Modulus,   Shear                                                       Damping Ratio,
                   Strain, %       G, ksf     Modulus, G/        Shearing Damping Ratiox,    after Peak
                                                                                                             D, after Peak
                                                                 Strain, %    D, %          Sheaering, ksf
                                                 Gmax                                                        Sheaering, %
                   4.06E-04        1958          1.01            4.06E-04     0.65                -*               -*
                   7.66E-04        1936          0.99            7.66E-04     0.75              1958             0.68
                   1.42E-03        1903          0.98            1.42E-03     0.98              1958             0.69
                   2.53E-03        1849          0.95            2.38E-03     1.12              1931             0.80
                   4.45E-03        1764          0.91            4.10E-03     1.35              1925             0.76
                   7.56E-03        1661          0.85            6.80E-03     1.77              1898             0.83
                   1.30E-02        1521          0.78            1.14E-02     2.17              1855             0.84
                   2.18E-02        1323          0.68            1.82E-02     3.12              1791             0.94
                     0.04          1148          0.59            3.04E-02     4.49              1781             1.10
                   6.59E-02         942          0.48            4.89E-02     5.90               -**              -**
                   1.11E-01         786          0.40            7.45E-02     7.42              1862             0.80
                     0.20           639          0.33            1.18E-01     11.17             2059             0.84
             +
                 Average Shearing Strain from the First Three Cycles of the Free Vibration Decay Curve
             x
           Average Damping Ratio from the First Three Cycles of the Free Vibration Decay Curve
         * Not Measured because Shearing Strain is Low
        ** Missed Resonance Measurement due to Ambient Noise at Small-Strain

Table A.5        Variation in Shear Modulus, Normalized Shear Modulus and Material Damping Ratio with Shearing Strain
                 from TS Tests of Reconstituted SM Specimen; Isotropic Confining Pressure (Loading), so' = 16 psi (2.3 ksf = 110 kPa)
                            First Cycle                                                   Tenth Cycle
   Peak            Shear       Normalized     Material       Peak                                      Material
                                                                     Shear Modulus, Normalized Shear
 Shearing        Modulus, G, Shear Modulus, Damping Ratio, Shearing                                  Damping Ratio,
                                                                         G, ksf     Modulus, G/Gmax
 Strain, %          ksf          G/Gmax        D, %        Strain, %                                    D, %
 3.75E-04            2099            1.00            0.71        3.75E-04         2107              1.01              0.60
 7.53E-04            2082            1.00            0.75        7.57E-04         2074              0.99              0.68
 1.34E-03            2042            0.98            1.10        1.35E-03         2037              0.97              0.96
 3.00E-03            1963            0.94            1.75        3.03E-03         1951              0.93              1.44
 6.43E-03            1822            0.87            2.98        6.49E-03         1810              0.87              2.38
 1.22E-02            1617            0.77            4.25        1.23E-02         1600              0.77              3.44
 2.64E-02            1339            0.64            7.82        2.66E-02         1328              0.64              6.64




                                                                  V. 23

				
DOCUMENT INFO
Shared By:
Categories:
Tags:
Stats:
views:0
posted:7/16/2014
language:English
pages:2