AISI 1008 Steel by le9vi1

VIEWS: 1,003 PAGES: 2

									                                             AISI 1008 Steel
   Subcategory: AISI 1000 Series Steel; Carbon Steel; Low Carbon Steel; Metal

   Key Words: UNS G10080, JIS G3141(96) SPCC, ASTM A29, ASTM A108, ASTM A510, ASTM
   A512, ASTM A513, ASTM A519, ASTM A545, ASTM A575, ASTM A576, ASTM A619, ASTM
   A620, ASTM A621, ASTM A622, ASTM A635, FED QQ-S-637 (C1008), FED QQ-S-698 (C1008),
   FED QQ-W-461, MIL SPEC MIL R-8814, MIL SPEC MIL S-11310 (CS1008,1008), SAE J1397,
   SAE J403, SAE J412, SAE J414, DIN 1.0204, UNI CB10 FU


   Component              Wt. %


   C                    Max 0.1
   Fe               99.31 - 99.7
   Mn                   0.3 - 0.5
   P                  Max 0.04
   S                  Max 0.05

   Material Notes:
   Usually produced as rimmed, capped, semikilled, and fully killed, Rimmed have exceptional cold
   fomability. Weldability (spot, projection, butt, and fusion) and brazeability are excellent.
   Applications include extruded, cold headed, cold upset, and cold pressed parts and forms.

Physical Properties                 Metric    English                                          Comments
Density                       7.872 g/cc 0.284 lb/in³         Composition 0.06% C, 0.38% Mn, 0.01% Si,
                                                                                     annealed at 925°C

Mechanical Properties
Hardness, Brinell                       86         86
Hardness, Knoop                        103        103                    Converted from Brinell hardness.
Hardness, Rockwell B                    49         49                    Converted from Brinell hardness.
Hardness, Vickers                       88         88                    Converted from Brinell hardness.
Tensile Strength, Ultimate     305 MPa       44200 psi
Tensile Strength, Yield        170 MPa       24700 psi
Elongation at Break                  30 %        30 %                                             in 50 mm
Reduction of Area                    55 %        55 %
Modulus of Elasticity          200 GPa       29000 ksi                                     Typical for steel
Bulk Modulus                   140 GPa       20300 ksi                                     Typical for steel
Poisson's Ratio                       0.29       0.29                                     Typical For Steel
Machinability                        55 %        55 %    Based on AISI 1212 steel. as 100% machinability.
                                                            The machinability of Group I bar, rod, and wire
                                                               products can be improved by cold drawing.
Shear Modulus                       80 GPa   11600 ksi                                     Typical for steel
                                         AISI 1010 Steel
Subcategory: AISI 1000 Series Steel; Carbon Steel; Low Carbon Steel; Metal

Key Words: UNS G10100, AMS 5040, AMS 5042, AMS 5044, AMS 5047, AMS 5053, ASTM
A29, ASTM A108, ASTM A510, ASTM A519, ASTM A545, ASTM A549, ASTM A575, ASTM
A576, MIL SPEC MIL-S-11310 (CS1010), JIS S 9 CK, SAE J403, SAE J412, SAE J414, DIN
1.1121, AFNOR XC 10 (Fr), JIS S10 C, JIS S 12 C

Component               Wt. %


C                 0.08 - 0.13
Fe              99.18 - 99.62
Mn                  0.3 - 0.6
P                   Max 0.04
S                   Max 0.05

Material Notes:
Easily cold formed by heading, extruding, upsetting, bending, and other deforming processes.
Uses for wires include electroplated products, such as racks, storage bins, shopping carts, fan
guards, and jewelry, and unplated such as wires, staples, hardware, and barbed wire.

Physical Properties             Metric    English                                        Comments
Density                     7.87 g/cc 0.284 lb/in³                                   Typical for steel

Mechanical Properties
Hardness, Brinell                  105        105
Hardness, Knoop                    123        123                  Converted from Brinell hardness.
Hardness, Rockwell B                60         60                  Converted from Brinell hardness.
Hardness, Vickers                  108        108                  Converted from Brinell hardness.
Tensile Strength, Ultimate 365 MPa       52900 psi
Tensile Strength, Yield     305 MPa      44200 psi
Elongation at Break              20 %        20 %                                           in 50 mm
Reduction of Area                40 %        40 %
Modulus of Elasticity       200 GPa      29000 ksi                                   Typical for steel
Bulk Modulus                140 GPa      20300 ksi                                   Typical for steel
Poisson's Ratio                   0.29       0.29                                   Typical For Steel
Machinability                    55 %        55 %                Based on AISI 1212 steel. as 100%
                                                      machinability. The machinability of Group I bar,
                                                     rod, and wire products can be improved by cold
                                                                                             drawing.
Shear Modulus                   80 GPa   11600 ksi                                   Typical for steel

								
To top